Icaflex®
Polyurethane systems from Icap Sira for Textiles.
Polyester and Polyether Polyurethanes for solvent based finishing systems.
Applications: Technical textiles, Synthetic leathers.
Grade |
Chemistry |
Base |
Solvents |
Solid Content % ± 1 |
Viscosity (mPa*s) |
Soft and Melt Temperature (°C) |
Mod. 100% (Kg/cm²) |
Mod. 300% (Kg/cm²) |
Tensile Strength (Kg/cm²) |
Elongation at Break (%) |
Applications |
ADB293 |
Aromatic |
Polyester |
A/TOL |
39 |
15,000 |
190 220 |
4 |
25 |
35 |
450 |
Soft adhesive PU, self-crosslinking, suitable for direct coating on garment fabrics. Dry touch. Good washing resistance. |
ADB589C |
Aromatic |
Polyester |
AE/ MEK/ TOL |
40 |
32,500 |
60 70 |
65 |
115 |
200 |
430 |
High crystallisation adhesive used for finishing and as thermoadhesive for lamination. Medium soft hand, high resistance to solvents and hydrolysis. |
ADB596 |
Aromatic |
Polyether |
EA |
40 |
32,500 |
NA |
NA |
NA |
NA |
NA |
Soft adhesives, suitable for coating. Very good resistance to hydrolysis, very soft hand. |
ADB562 |
Aromatic |
Polyester |
EA |
50 |
55,000 |
NA |
NA |
NA |
NA |
NA |
Soft adhesive, used in leather sector, suitable for transfer and direct coating. Good resistance to hydrolysis. |
ADB585 |
Aromatic |
Polyester |
EA |
45 |
55,000 |
NA |
40 |
70 |
380 |
630 |
Soft adhesive, used either for lamination or direct coating. Good resistance to hydrolysis. |
ADB588 |
Aromatic |
Polyester |
EA/ MEK |
35 |
6,500 |
60 70 |
60 |
70 |
170 |
800 |
High crystallisation adhesive, suitable for finishing and as thermoadhesive for laminating. Medium-soft hand, high resistance to solvents and hydrolysis. |
ADB595 |
Aromatic |
Polyester |
EA/ MEK |
40 |
32,500 |
NA |
NA |
NA |
NA |
NA |
Soft adhesives, suitable for transfer and direct coating. Very good resistance to hydrolysis. |
ADM383 |
Aromatic |
Polyester |
DMF |
50 |
75,000 |
160 170 |
25 |
60 |
120 |
870 |
Soft adhesive for garment articles and footwear. |
ADM511 |
Aromatic |
Polyether |
DMF |
50 |
50,000 |
130 140 |
20 |
30 |
60 |
850 |
Soft adhesive, recommended for one-coat-system. High resistance to solvents and hydrolysis. |
ADM614 |
Aromatic |
Polyether |
MEK |
39 |
22,500 |
120 130 |
10 |
13 |
16 |
800 |
Soft adhesive for garment articles and footwear. Excellent resistance to hydrolysis. |
ADM516 |
Aromatic |
Polyether |
DMF/ TOL |
40 |
50,000 |
170 180 |
25 |
50 |
150 |
1,000 |
Soft adhesive, general purpose, excellent resistance to hydrolysis. Adhesive for ICAFLEX® HS series. |
ADM625 |
Aliphatic |
Polyester |
A/ TOL |
35 |
40,000 |
170 180 |
35 |
60 |
400 |
800 |
Soft adhesive, used in garment sector. High lightfastness and resistance to hydrolysis. |
ADM535 |
Aromatic |
Polyester |
DMF/ TOL |
35 |
40,000 |
170 180 |
40 |
60 |
400 |
800 |
Medium soft adhesive suitable for furniture, footwear and leather sectors. Good resistance to solvents and good flexibility. Suitable for PVC. |
ADM912 |
Aliphatic |
Poly-carbonate |
DMF/ TOL |
35 |
40,000 |
170 180 |
40 |
95 |
450 |
600 |
Medium soft adhesive, suitable for transfer coating. Used when high lightfastness and resistance to hydrolysis are requested. |
BR447 |
Aliphatic |
PTHF |
A/ TOL |
30 |
30,000 |
170 180 |
20 |
35 |
180 |
1,000 |
Soft skin, breathable, suitable in direct and transfer coating for production of technical articles. Matt version available. |
BR464 |
Aromatic |
Polyester
Polyether |
TOL/ NMP |
30 |
70,000 |
160 170 |
90 |
290 |
560 |
520 |
Medium-soft skin, breathable, suitable in direct and transfer coating for production of technical articles. |
BR366 |
Aromatic |
Polyether |
EA/ MEK |
45 |
32,500 |
NA |
NA |
NA |
NA |
NA |
Soft adhesive, breathable, suitable in direct coating for production of technical articles. |
BR348 |
Aliphatic |
PTHF/
Polyether |
DMF |
30 |
42,500 |
170 180 |
80 |
150 |
420 |
640 |
Medium skin, breathable, suitable in direct coating and transfer for production of technical articles. |
BR359 |
Aliphatic |
Polyester
Polyether |
EA/ MP |
45 |
26,000 |
NA |
NA |
NA |
NA |
NA |
Medium adhesive, breathable, suitable in direct coating for production of technical articles. |
NE131 |
Aliphatic |
Polyester |
DMF |
30 |
42,500 |
180 200 |
30 |
65 |
400 |
700 |
Soft skin used for transfer coating applications. Suitable for garment articles. |
NE132 |
Aliphatic |
Polyester |
A/ TOL |
30 |
55,000 |
180 200 |
30 |
65 |
400 |
700 |
Soft skin used for transfer and direct coating applications. Suitable for garment articles. |
NE135 |
Aliphatic |
Polyester |
A/ TOL |
25 |
27,500 |
180 200 |
30 |
65 |
400 |
700 |
Soft skin for transfer and direct coating applications. Suitable for garment articles. |
NE125 |
Aliphatic |
Polyester |
DMF |
25 |
15,000 |
190 200 |
90 |
250 |
600 |
470 |
Medium skin, suitable for transfer coating applications. Dry touch, good abrasion and resistance to hydrolysis |
Icap-Sira’s formulations are compatible with the following textile standards (applicable to finished textile products):
OEKO-TEX® Standard 100, CLEAR TO WEAR ®, ECOLABEL®, Detox
Solvents: A = Alcohol, DMF = Dimethylformamide, EA, Ethyl Acetate, MEK = Methyl Ethyl Ketone, MPA = Methoxy Propyl Acetate, MP = Methoxy Propanol, TOL = Toluene.
Available Packaging: Drums, IBCs and Bulk*
*as part of our commitment to health and safety, a pre-bulk tank inspection of the facility will need to be carried out if applicable.
Polyester and Polyether Polyurethanes for solvent based finishing systems.
Applications: Technical textiles, Synthetic leathers.
Grade |
Chemistry |
Base |
Solvents |
Solid Content % ± 1 |
Viscosity (mPa*s) |
Soft and Melt Temperature (°C) |
Mod. 100% (Kg/cm²) |
Mod. 300% (Kg/cm²) |
Tensile Strength (Kg/cm²) |
Elongation at Break (%) |
Applications |
NE128 |
Aliphatic |
Polyester |
A/ TOL |
25 |
28,000 |
180 190 |
90 |
160 |
480 |
600 |
Medium skin, suitable for transfer coating applications. Dry touch, good resistance to abrasion and hydrolysis |
NE325 |
Aliphatic |
Poly-
carbonate |
A/ TOL |
25 |
28,000 |
190 210 |
120 |
400 |
480 |
350 |
Medium skin high lightfastness and resistance to hydrolysis. Suitable for transfer and direct applications for technical articles |
NE116 |
Aliphatic |
Polyester |
DMF |
25 |
30,000 |
195 200 |
140 |
290 |
530 |
480 |
Medium hard skin for transfer coating applications. Used for leathers, footwear and furniture. Suitable for “patent” articles. |
NE127 |
Aliphatic |
Polyester |
A/ TOL |
25 |
28,000 |
200 210 |
200 |
415 |
440 |
330 |
Hard skin used for transfer and direct coating applications when dry hand and high hardness are requested. Suitable for PU/PVC articles. |
NE118 |
Aliphatic |
Polyester |
DMF |
25 |
28,000 |
200 210 |
255 |
- |
470 |
270 |
Very hard skin used for transfer coating applications when dry hand and high hardness are requested. Suitable for PU/PVC articles. |
NE119 |
Aliphatic |
Polyester |
A/ TOL |
25 |
28,000 |
200 210 |
255 |
- |
470 |
270 |
Very hard skin used for transfer and direct coating applications when dry hand and high hardness are requested. Suitable for PU/PVC articles. |
NE138 |
Aliphatic |
Polyether |
A/ TOL |
30 |
30,000 |
220 230 |
70 |
180 |
500 |
650 |
Medium skin, suitable for transfer coating applications. Dry touch, good abrasion and hydrolysis resistance |
NE624 |
Aliphatic |
PTHF |
DMF |
30 |
28,000 |
180 200 |
45 |
105 |
440 |
630 |
Medium soft skin for transfer coating applications. Suitable for garment articles. Good flexural strength. |
SK215 |
Aromatic |
Polyester |
DMF |
35 |
45,000 |
150 170 |
40 |
60 |
400 |
800 |
Medium soft skin for transfer coating applications. Suitable for garment articles. Good flexural strength |
SK450 |
Aromatic |
Polyester |
DMF |
35 |
70,000 |
180 200 |
90 |
250 |
600 |
470 |
Medium skin, suitable for transfer coating applications. Dry touch, good abrasion and hydrolysis resistance |
SK290 |
Aromatic |
Polyester |
DMF |
35 |
115,000 |
190 200 |
50 |
100 |
550 |
750 |
Medium skin, general purpose. Good resistance to solvents and flexural strength. |
SK349 |
Aromatic |
Polyester |
DMF |
35 |
45,000 |
210 230 |
50 |
170 |
450 |
600 |
Medium soft skin especially suitable for footwear applications. It has good flexural strength and resistance to solvents and hydrolysis and very good adhesion on PVC |
HS510 |
Aromatic |
Polyether |
- |
100 |
45,000 |
NA |
130 |
260 |
280 |
320 |
Skin suitable for the production of technical articles, high resistance to hydrolysis. |
CG283Y |
Aromatic |
Polyester |
DMF |
35 |
95,000 |
180 200 |
210 |
400 |
580 |
460 |
Hard skin used for the production of hard PVC articles by wet-process. It is mainly used for articles for footwear, bags and leather goods. Good resistance to solvents |
|
|
|
|
|
|
|
|
|
|
|
|
|
Polyol Biocomponent Polyurethane systems from Icap Sira for Textiles.
Polyester and Polyether based pre-polymers. Polyester and Polyether based Polyol’s, which are listed under their solvent based solutions.
Biodegradable dispersions. This product range consists of modified starches and polyester based dispersions.
Applications: Technical textile modifier, impregnation, Medium-Hard hand.
Grade |
Base |
%NCO |
n°OH |
Viscosity Brookfield RVT mPas |
Comment |
BI PR100AR |
Prepolymers |
18 |
- |
2,500 |
Polyester based aromatic NCO-terminated prepolymer. |
BI PR200AL |
Prepolymers |
17.7 |
- |
600 |
Polyether based aliphatic NCO-terminated prepolymer. |
BI PR3300AR |
Prepolymers |
14.7 |
- |
2,000 |
Polyether based aromatic NCO-terminated prepolymer. |
BI PR400AL |
Prepolymers |
19.5 |
- |
3,500 |
Polyester based aliphatic NCO-terminated prepolymer from renewable sources. |
BI POL100PS |
Polyols |
- |
205 |
2,250 |
Polyester based polyol compound for medium soft films. |
BI POL200PE |
Polyols |
- |
420 |
350 |
Polyether based polyol compound for hard films. |
BI POL400PS |
Polyols |
- |
200 |
3,200 |
Polyester based polyol compound from thermoplastic renewable sources. |
BI POL600PE |
Polyols |
- |
140 |
750 |
Polyether based polyol compound for medium soft films. |
BI POL703PC |
Polyols |
- |
103 |
2,000 |
Polycarbonate based polyol compound for medium soft films. |
Please get in touch with our Resins and Specialities team by filling out the enquiry form below.
The information shown on this page(s) is intended as a product guide only; specification and properties of products are subject to change by the manufacturer and no guarantees or warranties are implied or inferred by the information provided here. It is the responsibility of the user to request the most current information and determine the suitability of any product in the user’s application.
*in line with our commitment to Responsible Care®, a pre-delivery safety inspection will generally be required prior to the first bulk delivery of a hazardous liquid.